Pwodwi Deskripsyon
JIS G3445 Kabòn Steel san pwoblèm mekanik tib
Poukisa JIS G3445 kabòn asye san pwoblèm tiyo asye gen yon avantaj nan jaden an nan machin?
1. Materyèl tiyo asye anba estanda JIS G3445 la se sitou ba -kabòn asye, tankou seri STKM11A/STKM13, ak yon ekivalan kabòn soude (CE) nan<0.35%, which can be welded without preheating, which can significantly reduce the processing cost. Compared with the same grade of carbon steel pipe, the cost is about 25% lower than ASTM A106 (because the high-temperature performance testing cost is saved).
2. STKM12C se pi bon chwa materyèl pou silenn idwolik. Tolerans JIS G3445 kabòn asye san pwoblèm tiyo asye kontwole nan ± 0.15mm atravè pwosesis la desen frèt, pandan y ap ASTM A53 mande pou fanm k'ap pile adisyonèl anba menm teknoloji a pwosesis. JIS G3445 te vin chwa pri -efikas pou mwens pase oswa egal a kò silenn idwolik 32MPa ak precision pwosesis desen frèt li yo.
3. JIS G3445 kabòn asye tiyo san pwoblèm sipòte pwosesis gwo twou san fon tankou Stamping ak koube, epi yo ka itilize pou parantèz chasi ak ankadreman kò fòme nan otomobil.
Aplikasyon
JIS G3445 Carbon Steel Seamless Mechanical Tube se apwopriye pou yon pakèt aplikasyon nan yon pakèt domèn endistri yo. Aplikasyon sa yo enkli:
- Pati otomobil:sistèm sispansyon, kolòn volan, arbr kondwi ak lòt konpozan estriktirèl.
- Pati machin:ankadreman, arbr ak angrenaj.
- Ekipman konstriksyon:boom teknik, konpozan pon ak lòt aplikasyon lou{0}.
- Jeni jeneral:ankadreman estriktirèl, sistèm CONVEYOR ak lòt aplikasyon mekanik.
Konpozisyon chimik
| Steel Klas | Konpozisyon chimik | |||
| STKM 11A | C: 0.12% maksimòm, Si: 0.35% maksimòm, Mn: 0.60% maksimòm, P: 0.040% maksimòm, S: 0.040% maksimòm | |||
| STKM 12A | C: 0.20% maksimòm, Si: 0.35% maksimòm, Mn: 0.60% maksimòm, P: 0.040% maksimòm, S: 0.040% maksimòm | |||
| STKM 12B | C: 0.20% maksimòm, Si: 0.35% maksimòm, Mn: 0.60% maksimòm, P: 0.040% maksimòm, S: 0.040% maksimòm | |||
| STKM 12C | C: 0.20% maksimòm, Si: 0.35% maksimòm, Mn: 0.60% maksimòm, P: 0.040% maksimòm, S: 0.040% maksimòm | |||
| STKM 13A | C: 0.25% maksimòm, Si: 0.35% maksimòm, Mn: 0.30-0.90%, P: 0.040% maksimòm, S: 0.040% maksimòm | |||
| STKM 13B | C: 0.25% max, Si: 0.35% max, Mn: 0.30-0.90%, P: 0.040% max, S: 0.040% max | |||
| STKM 13C | C: 0.25% max, Si: 0.35% max, Mn: 0.30-0.90%, P: 0.040% max, S: 0.040% max | |||
| STKM 15A | C: 0.25% max, Si: 0.35% max, Mn: 1.30% max, P: 0.040% max, S: 0.040% max | |||
Pwopriyete mekanik
| Steel Klas | Fòs rupture (MPa) | Sede fòs (MPa) | elongasyon (%) |
| STKM 11A | 290 min | 180 min | 25 min |
| STKM 12A | 345 min | 175 min | 35 min |
| STKM 12B | 390 min | 275 min | 25 min |
| STKM 12C | 470 min | 355 min | 20 min |
| STKM 13A | 375 min | 215 min | 30 min |
| STKM 13B | 440 min | 305 min | 20 min |
| STKM 13C | 510 min | 375 min | 20 min |
| STKM 15A | 470 min | 345 min | 20 min |
Klas altènatif posib
Pandan ke JIS G3445 espesifye yon seri konplè nan asye kabòn tib mekanik san pwoblèm, gen klas altènatif ki disponib nan lòt estanda entènasyonal yo. Gen kèk altènativ potansyèl yo konsidere yo se ASTM A519, DIN 2391, ak BS 6323.
Li esansyèl pou konsilte estanda ki enpòtan yo epi konpare pwopriyete materyèl ak espesifikasyon lè w ap konsidere klas altènatif pou aplikasyon espesifik.
Anbalaj
Yon fwa tiyo yo te pase tout enspeksyon ak tès yo, yo pare pou anbalaj. Yo anjeneral pake nan bal vlope nan plastik. Tiyo yo ka pake ak pare pou livrezon selon kondisyon kliyan, asire ke tiyo yo pwoteje pandan transpò epi anpeche domaj sifas yo.
Pwodwi Montre
Baj popilè: jis g3445 kabòn asye san pwoblèm tib mekanik, Lachin, Swèd, manifaktirè, faktori, Customized, wholesale, pri, OEM, moulen, pwodiktè, pou vann